RPL – HAC - 75 -
PRODUCT: | RPL – HAC – 75 | TYPE: | High Alumina Cement | NATURE OF BOND : | HYDRAULIC | APPLICATION: | For Manufacturing High Purity & High Density Castables. | | | GENERAL PROPERTIES | | RAW MATERIAL BASE: | CALCINED CLAY & BAUXITE. | MAX. SERVICE TEMP. | 15500C | MAX GRAIN SIZE: | As per requirement. | WATER REQ. FOR CASTING: | N.A. | REVERSIBLE THERMAL EXPANSION: | N.A. | | | CHEMICAL ANALYSIS,% | TYPICAL ACTUAL | AL2O3 | 72.00 72.00 min. | SiO2 | 0.5 - | FE2O3 | 0.50 0.75max | TiO2 | 4.30 - | CaO | 26.00 - | LOI | 0.20 - | | | PHYSICAL PROPERTIES | | CCS, kg/cm2 | | after drying at 1100C/24 hrs | | after heating at 8000C/3 hrs | | after heating at11000C/3 hrs | 600 (After 1 Days) | | | THERMAL PROPERTIES | | Refractoriness, Orton/0C | +31/+1683 +31/+1683 min. | | | Packaging: | 50 Kg bags | Storage life: | 6 months | Delivery state: | Dry |
|